The ferrite  content,in  percentage  by  surface/volume  fraction,shall  be  as  stated  below  for  all  duplex  grades:

鐵素體含量，以表麵/體積分數的百分比表示，應如下所述，適用於所有雙相等級：

—35%to   60%in   base   material;

— 基材中為35%至60%;

—35%to  65%in  solution   heat   treated  weld   metals;

—在固溶熱處理的焊接金屬中為35%至65%;

—30%to  70%for  welds   in  the  as  welded  condition.

一對於處於焊接狀態的焊縫，30%至70%。